Creep-fatigue interactions in pure Tantalum under constant and variable amplitude
Communication sans acte
Due to its specific mechanical properties, tantalum is often used in strength-demanding military applications. High cycle fatigue (HCF) behaviour of pure tantalum, however, has been rarely reported and the mechanisms at stake to account for deformation under cyclic loadings are still badly understood [1-2]. This presentation aims at better understanding the HCF damage mechanisms encountered in pure tantalum under such loadings. HCF loadings at various frequencies were performed in tension at room temperature on commercially-pure tantalum. Mean stress effects and frequency effects were investigated in the aim of clarifying the interaction between fatigue and creep. For symmetrical loadings (R=-1, i.e. under zero mean stress), fracture mechanisms were observed to vary from intergranular to transgranular when the maximum stress was decreased. For non-symmetrical loadings (R>0, with sufficiently large mean stress), a transition was also observed from extensive necking to intergranular initiation. Important creep activation was deduced from the presence of necking. This prevalence of creep at room temperature was actually confirmed by two other phenomena: a) The large influence of the frequency on fatigue life, indicating time-dependent damage. b) Important creep deformation during room-temperature creep tests. Finally, complex sequential loadings, representative of in-service loadings, were applied to pure tantalum specimens. The contribution of each loading sequence to the overall damage was quantified. It was shown that linear cumulative damage rules (analogous to Miner’s law to account for fatigue damage and for creep damage) failed to predict life duration of pure tantalum. The ONERA model [3-4], which specifically accounts for creep-fatigue interactions, granted better results. However, it is important to notice that this model uses engineering stresses as input, assuming that the specimen cross-section does not evolve drastically during fatigue/creep deformation. Such hypothesis needs to be revisited as the true stress seems a more realistic input to account for creep damage.
Showing items related by title, author, creator and subject.
Article dans une revue avec comité de lectureMARECHAL, David; SAINTIER, Nicolas; PALIN-LUC, Thierry; NADAL, François (Trans Tech Publications, 2014)Due to its specific mechanical properties, tantalum is often used in strength-demanding military applications. High-cycle fatigue (HCF) behaviour of pure tantalum, however, has been rarely reported and the mechanisms at ...
Internal fatigue crack monitoring during ultrasonic fatigue test using temperature measurements and tomography Article dans une revue avec comité de lectureRANC, Nicolas; MESSAGER, Alexandre; JUNET, A.; PALIN-LUC, Thierry; BUFFIÈRE, J.Y.; SAINTIER, Nicolas; ELMAY, Wafa; MANCINI, L.; KING, A.; NADOT, Yves (Elsevier, 2022-09)Very high cycle fatigue fracture is often associated with internal crack propagation and one major problem to study the initiation and the propagation of this internal crack is to detect its initiation and quantify its ...
In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth Article dans une revue avec comité de lectureMESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves; RANC, Nicolas (Wiley-Blackwell, 2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...
About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading Article dans une revue avec comité de lectureBecause of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermomechanical ...
About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading Article dans une revue avec comité de lectureBecause of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermo-mechanical ...