In situ analysis of the influence of twinning on the strain hardening rate and fracture mechanism in AZ31B magnesium alloy
TypeArticles dans des revues avec comité de lecture
The influence of twinning on the strain hardening rate and fracture mechanism in AZ31B magnesium alloy was studied in this work by in situ microstructural analysis during tensile testing in a chamber of scanning electron microscope. Three types of samples used in this study were obtained by (1) extrusion (as-supplied), (2) I-ECAP and (3) I-ECAP followed by side upsetting. Microstructures, textures and mechanical properties were examined after each processing step. An analytical equation was used to describe flow stress curves of the samples which exhibited various modes of deformation (1) only by slip, (2) dominated by tensile twinning followed by slip and (3) dominated by contraction twinning followed by slip. It was shown that tensile twinning increases strain hardening rate, while the opposite is observed for contraction twinning. The effective Schmid factors for slip in volumes deformed by tensile and contraction twinning were determined in this work using modelling approach as 0.215 and 0.45, respectively. Contraction twinning was also revealed to be responsible for an earlier fracture of the extruded sample subjected to tension, since microcracking was shown explicitly to be initiated within twins.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
In situ analysis of the influence of twinning on the strain hardening rate and fracture mechanism in AZ31B magnesium alloy GZYL, Michal; PESCI, Raphaël; ROSOCHOWSKI, Andrzej; BOCZKAL, Sonia; OLEJNIK, Lech (Springer, 2015)The influence of twinning on the strain hardening rate and fracture mechanism in AZ31B magnesium alloy was studied in this work by in situ microstructural analysis during tensile testing in a chamber of scanning electron ...
GZYL, Michal; ROSOCHOWSKI, Andrzej; PESCI, Raphaël; OLEJNIK, Lech; YAKUSHINA, Evgenia; WOOD, Paul (Springer, 2014)Incremental equal channel angular pressing (I-ECAP) is a severe plastic deformation process used to refine grain size of metals, which allows processing very long billets. As described in the current article, an AZ31B ...
Dose, image quality and spine modeling assessment of biplanar EOS micro-dose radiographs for the follow-up of in-brace adolescent idiopathic scoliosis patients. MOREL, Baptiste; MOUEDDEB, Sonia; BLONDIAUX, Eleonore; RICHARD, Stephen; BACHY, Manon; VIALLE, Raphael; LE POINTE, Hubert Ducou (Springer, 2018)Purpose: The aim of this study was to compare the radiation dose, image quality and 3D spine parameter measurements of EOS low-dose and micro-dose protocols for in-brace adolescent idiopathic scoliosis (AIS) patients. ...
Thermo-mechanical behaviour of TRIP 1000 steel sheets subjected to low velocity perforation by conical projectiles at different temperatures RODRIGUEZ MARTINEZ, José Antonio; PESCI, Raphaël; RUSINEK, Alexis; ARIAS, Angel; ZAERA, Ramon; PEDROCHE, David Arias (Elsevier, 2012)This paper presents and analyzes the behaviour of TRIP 1000 steel sheets subjected to low velocity perforation by conical projectiles. The relevance of this material resides in the potential transformation of retained ...
Effets des échanges thermiques sur l'écoulement de l'alliage semi-solide mis en forme par thixoextrusion BECKER, Eric; GU, Guochao; LANGLOIS, Laurent; PESCI, Raphaël; BIGOT, Régis (Association Française de Mécanique, 2011)Le comportement d’un alliage mis en forme à l’état semi-solide n’est toujours pas bien compris. Afin d’établir l'influence de différents paramètres sur l'écoulement de la matière, un processus de thixoextrusion expérimental ...