Tribological response of AA 2024-T3 aluminium alloy coated with a DLC duplex coating
Article dans une revue avec comité de lecture
Auteur
Date
2015Journal
Tribology InternationalRésumé
Considerable improvement in the tribological response was achieved during sliding wear tests against alumina ball, when AA 2024-T3-aluminium alloy substrate was coated with DLC/NiP duplex coating. Quantitative EPMA analysis carried out on the coated sample cross-section coupled with nanoindentation techniques allowed the identification of the coated system architecture as composed of 4 main layers, with distinct mechanical properties, on top of the aluminium substrate: DLC (a:C-H chromium dopped layer and graded layer of CrC), a newly formed graded layer of CNiPCr, product of the interdifusion during PVD processing, and the NiP coating. The change in the elastic modulus with penetration depth was described by means of an original approach that was developed for its specific application to multilayer coatings.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureKOSSMAN, Stephania; CHICOT, Didier; DECOOPMAN, Xavier; IOST, Alain; VAN GORP, Adrien; MEILLOT, E.; PUCHI-CABRERA, Eli-Saul; SANTANA, Y.Y.; STAIA, Mariana (ASM International/Springer, 2014)Nanostructured yttria-stabilized zirconia coatings for applications in high-temperature environments can be deposited by suspension plasma spraying (SPS) techniques. The present research has been conducted in order to study ...
-
Communication avec acteSTAIA, Mariana; TROCELIS, A; ZAIRI, Amel; SUAREZ, M; PUCHI-CABRERA, Eli-Saul; IOST, Alain; MONTAGNE, Alex (2016)The present work has been conducted in order to assess the mechanical and tribological performance of a ZrN coating deposited onto a H13 steel substrate by means of a closed field unbalanced magnetron-sputtering ion-plating ...
-
Article dans une revue avec comité de lectureSTAIA, M.H.; PUCHI-CABRERA, Eli-Saul; IOST, Alain; CARRASQUERO, E.; SANTANA, Y.Y.; LA BARBERA-SOSA, J.G.; CHICOT, Didier; VAN GORP, Adrien (Elsevier, 2013)This paper reports the results obtained from the study of friction and sliding wear in two corrosive solutions of an a-C:H coating deposited on 316L stainless against an alumina ball, employed as static counter part. ...
-
Communication sans actePUCHI-CABRERA, Eli-Saul; STAIA, Mariana; IOST, Alain (2015)The change in the composite hardness with penetration depth derived from nanoindentation tests conducted on coated systems, which involve the deposition of multilayer coatings, in general exhibit a complex ...
-
Article dans une revue avec comité de lecturePUCHI-CABRERA, Eli-Saul; STAIA, Mariana; IOST, Alain (ELSEVIER, 2015)The change in the composite hardness with penetration depth derived from nanoindentation tests conducted on coated systems, which involve the deposition of multilayer coatings, in general exhibits a complex shape, as a ...