CUETO, Elias; ABISSET-CHAVANNE, Emmanuelle; CHINESTA SORIA, Francisco (Wiley, 2019)
It is well known that model order reduction techniques that project the solution of the problem at hand onto a low-dimensional subspace present difficulties when this solution lies on a nonlinear manifold. To overcome these ... -
Article dans une revue avec comité de lecture; ; ; ; ; ;COLIN, Xavier (Elsevier, 2019)
The water sorption properties (i.e. diffusivity and solubility) of three unfilled vulcanized EPDMs were investigated in wet atmosphere (typically between 0 and 95% RH) and in pure distilled water (denoted as 100% RH) at ...
-
Article dans une revue avec comité de lecture; ;REGNIER, Gilles; FAYOLLE, Bruno (Elsevier, 2010)
The thermo-oxidation process at low temperatures for a montmorillonite- nanoreinforced polypropylene (PP) was studied. Experimental aging kinetic data at 100, 80 and 60 °C have been obtained and compared with a computational ...
-
Article dans une revue avec comité de lecture; ; ;GUSKOV, Mikhail (EDP Sciences, 2010)
Squeeze film dampers (SFD) are used to reduce dynamical loads in rotating machinery or to improve their performances in numerous industrial applications. The present paper considers the response of a dual shaft system with ...
-
Article dans une revue avec comité de lecture(Elsevier, 2011)The study of oxidation kinetics of isooctyl-3-(3,5-di-tert-butyl-4- hydroxyphenyl)propionate (Irganox 1135) stabiliser was carried out using silicone oil as an inert substrate. The stabiliser was exposed at 80-120 °C under ...
-
Article dans une revue avec comité de lecture(Elsevier, 2011)The reaction of 2,2′-methylene-bis(4-methyl-6-tert-butylphenol) stabiliser with oxygen was studied in an inert substrate at 80-120°C temperature under 0.02-3.0 MPa oxygen pressure ranges. UV/VIS spectrophotometry and Gel ...
-
Article dans une revue avec comité de lectureMAREAU, Charles; ; ; ; FAVIER, Véronique (EDP Sciences, 2010)
A newmicromechanical modelling is proposed to correlate some microstructural parameters and dissipation in ferritic steels under cyclic loading.We assumed the occurrence of two dissipative mechanisms associated with anelastic ...