Tribological and electrochemical performances of Cr/CrN and Cr/CrN/CrAlN multilayer coatings deposited by RF magnetron sputtering
Article dans une revue avec comité de lecture
CrN/CrAlN and Cr/CrN/CrAlN multilayers were grown with dual RF magnetron sputtering. The application of these multilayers will be wood machining of green wood. That is why ball-on-disc and electrochemical tests in NaCl aqueous solution were realized to elucidate the tribological and corrosion behavior of these coatings as they will be exposed to wear and corrosion during wood machining process. The samples/alumina and samples/WC coupling showed different wear mechanisms. The 300 nm thick Cr/CrN/CrAlN multilayer demonstrated the best tribological behavior and corrosion resistance. The influence of growth defects on corrosion resistance has been shown.
Files in this item
Showing items related by title, author, creator and subject.
Article dans une revue avec comité de lectureBOUZID, Kheireddine; BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne (the Serbian Tribology Society, 2015)A comparative study was conducted to evaluate the performances against wear and corrosion of CrN, CrMoN, CrZrN, CrVN single layer thin films. The latest are synthesized onto steel substrates (DIN 90CrMoV8), using R.F ...
Article dans une revue avec comité de lectureRAMOUL, Chams Eddine; BELIARDOUH, Nasser Eddine; BAHI, R.; NOUVEAU, Corinne; DJAHOUDI, Abdelghani; WALOCK, Michael J. (2018)Zirconium nitride (ZrN) thin films were deposited by reactive RF magnetron sputtering on Ti-6Al-4V and Si (100) substrates for potential use in biomedical applications. The tribological behaviour was evaluated against ...
A study of the wear performance of duplex treated commercial low-alloy steel against alumina and WC balls Article dans une revue avec comité de lectureBELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; WALOCK, Michael J.; JACQUET, Philippe (Elsevier, 2014)The objective of this work is to study the improvement of the tribological properties of low alloy steel using a duplex treatment of lowpressure carburizing and the deposition of a Cr–(WC–Co) coating by dual RF magnetron ...
Article dans une revue avec comité de lectureTLILI, Brahim; NOUVEAU, Corinne; WALOCK, Michael J.; NASRI, Mustapha; GHRIB, Taher (Elsevier, 2012)Cr/CrN/CrAlN, CrN/CrAlN and Cr/CrN thin layers were deposited by PVD (Physical Vapor Deposition). The multilayers were obtained from the combined deposition of different layers Cr, CrN and CrAlN thick films on on AISI4140 ...
Article dans une revue avec comité de lectureBELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Scientific Bulgarian Communications Ltd, 2014)The sliding tribological behaviour of Cr-(WC-Co) coating against wood (beech) as counterpart was investigated using a duplex treatment of low carbon steel(DIN 18CrMo4). The duplex treatment consists of LPC (low pressure ...