A study of the wear performance of duplex treated commercial low-alloy steel against alumina and WC balls
TypeArticles dans des revues avec comité de lecture
The objective of this work is to study the improvement of the tribological properties of low alloy steel using a duplex treatment of lowpressure carburizing and the deposition of a Cr–(WC–Co) coating by dual RF magnetron sputtering. The treatments result in a 500 μm thick carburized layer and a sputtered coating thickness of ~2 μm. Tribological tests were made with a ball-on-disk tribometer under dry conditions with low load and low speed. The worn surfaces of the disk, the wear counterpart, and resulting debris were analyzed by X-ray diffraction, optical microscopy, optical profilometry, and a scanning electron microscope equipped with an energy-dispersive X-ray spectrometer. The wear performance of the samples was evaluated in terms of wear rates and friction oefficients during the sliding processes against two different counterparts. Experimental results have shown that sliding wear, of the investigated duplex treated low alloy steels, is strongly dependent on the counterface materials. Under testing conditions, the overallwear performance of a Cr–WCcoating (Cr/Wratio of 1.12:1) deposited onto the surface of a carburized lowalloy steel (0.61wt.% C; HV=654±5) can be recommended as the best. The duplex-treated samples suffered severe, concentrated wear when against alumina. Thiswear is characterized by a combination of delamination, mild abrasion and oxidative wear. However, the wear mechanism seems to be oxidative and adhesive when against WC balls.
Files in this item
Showing items related by title, author, creator and subject.
Tribological and electrochemical performances of Cr/CrN and Cr/CrN/CrAlN multilayer coatings deposited by RF magnetron sputtering BELIARDOUH, Nasser Eddine; BOUZID, Kheireddine; NOUVEAU, Corinne; TLILI, Brahim; WALOCK, Michael J. (Elsevier, 2015)CrN/CrAlN and Cr/CrN/CrAlN multilayers were grown with dual RF magnetron sputtering. The application of these multilayers will be wood machining of green wood. That is why ball-on-disc and electrochemical tests in NaCl ...
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Scientific Bulgarian Communications, 2014)The sliding tribological behaviour of Cr-(WC-Co) coating against wood (beech) as counterpart was investigated using a duplex treatment of low carbon steel(DIN 18CrMo4). The duplex treatment consists of LPC (low pressure ...
BOUZID, Kheireddine; BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne (University of Kragujevac, 2015)A comparative study was conducted to evaluate the performances against wear and corrosion of CrN, CrMoN, CrZrN, CrVN single layer thin films. The latest are synthesized onto steel substrates (DIN 90CrMoV8), using R.F ...
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Emerald Group, 2016)Purpose – The purpose of this technical paper is to investigate the friction and wear behavior of inexpensive and durable cutting tools, developed for wood machining using duplex treatment. Design/methodology/approach – ...
GRAIRIA, Amina; BELIARDOUH, Nasser Eddine; ZAHZOUH, Moussa; NOUVEAU, Corinne; BESNARD, Aurélien (IOP Puiblishing, 2018)WCparticles reinforced Fe-based metal matrix composites were synthesized by powder metallurgy process. The microstructure and composition of the specimens were analyzed and the wear-resistant properties againstWCand alumina ...