Qualification of the damage induced by friction using X-ray Diffractometry
Communication sans acte
Auteur
FABRE, Agnès BARRALLIER, Laurent JÉGOU, SébastienRésumé
In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven [1]. The purpose of this study is to complete this research in order to develop a method to quantify the damage induced by the friction loading. (...)
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Communication sans acteFABRE, Agnès; BARRALLIER, Laurent; JÉGOU, Sébastien (2014)
Le rodage est un phénomène présent lors des premiers cycles de frottement qui modifie la surface de contact d’une pièce d’un point de vue géométrique, couplé à des modifications de propriétés mécaniques. Le rodage génère ...
-
Communication sans acteFABRE, Agnès; BARRALLIER, Laurent; JÉGOU, Sébastien (2014)
In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven [1]. The purpose of this study is to complete this research in order to develop a method to ...
-
Article dans une revue avec comité de lecture; ; ;FABRE, Agnès; BARRALLIER, Laurent (Elsevier, 2013)
Micropitting is a form of surface fatigue damage that occurs in the gear teeth. It is due to the effect of variation in the mechanical loading in the contact zone between the two teeth, induced especially by flank roughness. ...
-
Article dans une revue avec comité de lecture; ;FABRE, Agnès; BARRALLIER, Laurent; JACQUET, Philippe (Springer Verlag, 2014)
The effect of the composition of two steels (B and 6MnCr5) on precipitation of undesirable phases (carbides, nitrides and carbonitrides) under thermochemical treatment (low-pressure or vacuum carbonitriding) is investigated. ...
-
Communication avec acte; ; ;BARRALLIER, Laurent; JÉGOU, Sébastien (2015)
In this study, Stress Corrosion Cracking (SCC) produced for 304L austenitic stainless steel in different concentrations of chloride containing sulfuric acid solutions was analyzed using both Scanning Electron Microscope ...