Thermal oxidation of vinyl ester and unsaturated polyester resins
Type
Articles dans des revues avec comité de lectureDate
2016Journal
Polymer Degradation and StabilityAbstract
The thermal oxidative ageing of vinyl ester and unsaturated polyester was studied at temperatures ranging from 120 to 160°C and oxygen pressures ranging from 0.02 to 2.0 MPa. The oxidation of both materials was shown to generate anhydrides detected by FTIR spectroscopy, the origin of which being the oxidation of CH group in <alpha> position of ester, and significant mass loss. According to FTIR study, vinyl ester was shown to be more oxidizable than unsaturated polyesters but this feature is counterbalanced by a lower volatile yield. The thickness of oxidized layer in diffusion limited oxidation regime was hence observed to be higher in Unsaturated Polyester (ca 600 µm) than in Vinyl Ester (ca 200 µm) at 160°C and seems not affected by the presence of high content of fillers.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
MONTANA, Juan-Sebastian; ROLAND, Sébastien; RICHAUD, Emmanuel; MIQUELARD-GARNIER, Guillaume (Elsevier, 2018)Multilayer coextrusion was used to obtain nanolayered films of self-assembled commercial triblock copolymer poly(methyl methacrylate-b-butyl acrylate-b-methyl methacrylate) (MAM) confined by poly(methyl methacrylate) (PMMA). ...
-
MONTANA, Juan Sebastian; ROLAND, Sébastien; MIQUELARD GARNIER, Guillaume; RICHAUD, Emmanuel (Elsevier, 2017)This paper reports an investigation of the thermal degradation of a poly(styrene-b-butadiene-b-methyl methacrylate) triblock terpolymer compared with those of butadiene rubbers and poly(styrene-b-methyl methacrylate). ...
-
MONTANA, Juan-Sebastian; MIQUELARD-GARNIER, Guillaume; RICHAUD, Emmanuel; ROLAND, SEBASTIEN (Elsevier, 2018)Multilayer coextrusion was used to obtain nanolayered films of self-assembled commercial triblock copolymer poly(methyl methacrylate-b-butyl acrylate-b-methyl methacrylate) (MAM) confined by poly (methyl methacrylate) ...
-
RICHAUD, Emmanuel; DJOUANI, Fatma; FAYOLLE, Bruno; VERDU, Jacques; FLACONNECHE, Bruno (Institut Français du Pétrole, 2015)This paper deals with polymer-fuel interaction focusing on specific effects of biofuels on polyethylene (PE) in automotive applications. The practical objective is to develop a predictable approach for durability of ...
-
Influence de la préoxydation d’un PEHD sur l’extraction des carbonyles et la croissance d’un biofilm PONS, C; FARCAS, F; RICHAUD, Emmanuel; FAYOLLE, Bruno; BOUCHEZ, T; MAZEAS, L (EDP Sciences, 2012)Les géomembranes en polyéthylène haute densité (PEHD) sont utilisées comme barrière d’étanchéité dans les Installations de Stockage de Déchets Non Dangereux (ISDND). Malgré les bonnes propriétés initiales du PEHD, face aux ...