Structural and mechanical properties of Cr–Zr–N coatings with different Zr content
TypeArticles dans des revues avec comité de lecture
Cr–Zr–N films have been synthesised using R.F reactive magnetron sputtering system on Si (100) wafer and XC100 steel substrate without heating. The structural, mechanical and friction coefficient evolution as a function of the Zr content were investigated by XRD, (EDS, WDS), WPS, XPS, SEM, AFM, nanoindentation, Scratch adhesion and pin-on-disc sliding wear tests. The results show, that, with increasing Zr content, the film structure changed with the coexistence of (Cr–N, Zr–N) crystallographic orientation mixture. The films formed a (Cr, Zr) N solid solution where Zr atoms substitute Cr atoms. CrN lattice parameter increased from 4.17 to 4.32 Å with the crystallite size refinement. The mechanical parameters (H, σ, E, H/E and H3/ E2) were significantly improved in comparison to binary films, especially at 29 at.-% Zr. The friction and wear behaviour of the Cr–Zr (29 at.-% Zr)–N coating also showed a significant improvement.
Showing items related by title, author, creator and subject.
Synthesis, microstructural and tribological characterization of calcined nano-bioceramic α- al2o3, sintered at different temperatures FELLAH, Mamoun; AISSANI, Linda; LABAIZ, Mohamed; NOUVEAU, Corinne; IOST, Alain; MONTAGNE, Alex; ABDUL SAMAD, Mohamed; LAKMINE, F. (2016)The current research was undertaken to study the improvement of the tribological behavior of nanocrystalline bioceramic, α-alumina sample, produced by the calculations of gibbsite at different temperatures (300 to 1200°C), ...
FELLAH, Mamoun; AISSANI, Linda; ZAIRI, Amel; ABDUL SAMAD, Mohamed; NOUVEAU, Corinne; TOUHAMI, Mohamed Zine; DJEBAILI, Hamid; MONTAGNE, Alex; IOST, Alain (Informa UK Limited, 2018)In the present study, the effect of thermal treatment on the mechanical and structural properties of chromium carbide coatings with different thicknesses is evaluated. The coatings were deposited by cathodic magnetron ...
Effect of Replacing Vanadium by Niobium and Iron on the Tribological Behavior of HIPed Titanium Alloys FELLAH, Mamoun; AISSANI, Linda; ABDUL SAMAD, Mohammed; IOST, Alain; MOHAMED ZINE, Touhami; MONTAGNE, Alex; NOUVEAU, Corinne (Springer, 2017)This study aims to examine the effect of replacing vanadium by niobium and iron on the tribological behavior of hot-isostatic-pressed titanium alloy (Ti–6Al–4V) biomaterial, using a ball-on-disk-type oscillating tribometer, ...
FELLAH, Mamoun; AISSANI, Linda; ABDUL SAMAD, Mohammed; PURNAMA, Agung; DJEBAILI, Hamid; MONTAGNE, Alex; IOST, Alain; NOUVEAU, Corinne (Wiley, 2018)Nanostructured Cr‐Zr‐N thin film with different Zr content (0 to 48.8 at.%) was deposited, using an RF magnetron‐sputtering technique. The structural evolution and morphological changes were performed. The tribological ...
FELLAH, Mamoun; AISSANI, Linda; ABDUL SAMAD, Mohamed; MECHACHETI, Said; TOUHAMI, Mohamed Zine; MONTAGNE, Alex; IOST, Alain (Taylor Francis, 2017)Binary Cr-N, Zr-N and Cr-Zr-N films were synthesised using a R.F. reactive magnetron sputtering technique by co-sputtering Cr and Zr. The crystalline structure, morphology, mechanical and tribological properties of the ...