Experimental and Theoretical Study of Multiscale Damage-Failure Transition in Very High Cycle Fatigue
TypeArticles dans des revues avec comité de lecture
Multiscale mechanisms of failure of metals (Armco iron, titanium, aluminum) are studied for high cycle and very high cycle fatigue. By correlating with the results of structural studies, a theoretical approach is developed to describe fatigue crack kinetics in damaged material under high cycle and very high cycle fatigue loading conditions. Stages of crack nucleation and propagation are analyzed using the profilometry data from the fracture surface. The scale invariance of fracture surface roughness is established, which allows an explanation of the self-similar nature of fatigue crack kinetics under high cycle and very high cycle fatigue. Variation of elastic-plastic properties of Armco iron under very high cycle fatigue is studied using an acoustic resonance method. It is found that the material density decreases during fatigue damage accumulation, with the minimum of the material density in the bulk of the specimen.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
OBORIN, V.; BANNIKOV, M.V.; NAIMARK, O.B; PALIN-LUC, Thierry (Pleiades Publishing, 2010)The role of the collective behavior of defect ensembles at the crack tip and the laws of fatigue crack propagation in R4 high strength steel have been studied under conditions of symmetric tension–compression gigacycle ...
OBORIN, V.; BANNIKOV, M.V.; NAIMARK, O.B; PALIN-LUC, Thierry (Wiley, 2010)The role of the collective behavior of defect ensembles at the crack tip and the laws of fatigue crack propagation in R4 high-strength steel have been studied under conditions of symmetric tension-compression gigacycle ...
PLEKHOV, O.A; PALIN-LUC, Thierry; SAINTIER, Nicolas; UVAROV, S. V.; NAIMARK, O.B (Blackwell, 2005)The present work is devoted to the investigation of fatigue crack initiation and growth in middle-cycle fatigue (∼105 cycles). Smooth specimens made of 35CrMo4 quenched and tempered steel were loaded in fully reversed plane ...
PLEKHOV, O.A; NAIMARK, O.B; SAINTIER, Nicolas; PALIN-LUC, Thierry (Pleiades Publishing, 2009)The structural and thermodynamic features of the elastic–plastic transition in armco iron and its plastic deformation are studied. Energy storage in iron is shown to have a nonlinear character and be accompanied by wavelike ...
Theoretical analysis, infrared and structural investigations of energy dissipation in metals under cyclic loading PLEKHOV, O.A; SAINTIER, Nicolas; PALIN-LUC, Thierry; UVAROV, S. V.; NAIMARK, O.B (Elsevier, 2007)The infrared and structural investigations of energy dissipation processes in metals subjected to cyclic loading have given impetus to the development of a new thermodynamic model with the capability of describing the ...