Analysis of laser–melt pool–powder bed interaction during the selective laser melting of a stainless steel
TypeArticles dans des revues avec comité de lecture
The laser powder bed fusion (LPBF) or powder-bed additive layer manufacturing process is now recognized as a high-potential manufacturing process for complex metallic parts. However, many technical issues are still to overcome for making LPBF a fully viable manufacturing process. This is the case of surface finish and the systematic occurrence of porosities, which require postmachining steps. Up till now, the porosity origin remains unclear but is expected to be related to the stability of the process. As a LPBF part is made by the accumulation of hundreds of meters of small weld beads, it also appears to be important to understand all the phenomena that occur during the laser-powder-melt pool (MP) interaction for each single track. For this reason, in the first part of our study, using an instrumented LPBF setup and a fast camera analysis (>10 000 image/s), single tracks were fabricated and analyzed in real time and postmortem. Spatters ejections and powder denudation phenomena were observed together with variations of melt pool dimensions and melt-pool instabilities. In turn, the physical origin of this powder denudation and the dynamics of the MP were investigated and discussed.
Showing items related by title, author, creator and subject.
Analysis and possible estimation of keyhole depths evolution, using laser operating parameters and material properties FABBRO, Rémy; DAL, Morgan; PEYRE, Patrice; COSTE, Fredéric; SCHNEIDER, MATTHIEU; GUNENTHIRAM, V (Laser Institute of America, 2018)The authors propose an analysis of the effect of various operating parameters on the keyhole depth during laser welding. The authors have developed a model that uses the analysis of the thermal field obtained in 2D geometry, ...
Experimental analysis of spatter generation and melt-pool behavior during the powder bed laser beam melting process GUNENTHIRAM, V; PEYRE, P; SCHNEIDER, MATTHIEU; DAL, Morgan; COSTE, Fredéric; KOUTIRI, Imade; FABBRO, Rémy (Elsevier, 2018)The experimental analysis of spatter formation was carried out on an instrumented SLM set-up allowing the quantification of spatter ejections and possible correlation with melt-pool behavior. Considering nearly similar SLM ...
PEYRE, Patrice; BERTHE, Laurent; DAL, Morgan; POUZET, Sébastien; SALLAMAND, Pierre; TOMASHCHUK, Iryna (Elsevier, 2014)Laser-induced reactive wetting and brazing of T40 titanium with A5754 aluminum alloy with 1.5 mm thickness was carried out in lap-joint conﬁguration, with or without the use of Al5Si ﬁller wire. A 2.4 mm diameter laser ...
PEYRE, Patrice; BERTHE, Laurent; DAL, Morgan; POUZET, Sébastien; SALLAMAND, Pierre; TOMASHCHUK, Iryna (Elsevier, 2014)Laser-induced reactive wetting and brazing of T40 titanium with A5754 aluminum alloy with 1.5 mm thickness was carried out in lap-joint configuration, with or without the use of Al5Si filler wire. A 2.4 mm diameter laser ...
PEYRE, Patrice; DAL, Morgan; POUZET, S Ebastien; CASTELNAU, Olivier (Laser Institute of America, 2017)The laser metal deposition (LMD) laser technique is a free-form metal deposition process, which allows generating near net-shape structures through the interaction of a powder stream and a laser beam. A simplified numerical ...