Local electrochemical impedance spectroscopy study of the influence of ageing in air and laser shock processing on the micro-electrochemical behaviour of AA2050-T8 aluminium alloy
TypeArticles dans des revues avec comité de lecture
In the present paper, the micro-electrochemical behaviour of AA2050-T8 in 0.1 M NaCl was first studied after polishing by means of local electrochemical impedance spectroscopy and field-emission scanning electron microscopy/electron dispersive spectroscopy (FE-SEM/EDS). The influence of ageing in air and LSP was then investigated. Ageing in air for three months led to an increase in the charge transfer resistance. This was clearly observed in sites surrounding constituent particles where the charge transfer resistance was in the order of 1 MΩ cm2 (instead of 10-3 MΩ cm2 after polishing). Increased passivity around particles was confirmed from FE-SEM/EDS analysis. On the other hand, the effect of LSP on the behaviour of the matrix was found to be extremely beneficial. Both charge transfer and oxide film resistances were sharply increased to approximately 0.35 MΩ cm 2 and 1 MΩ cm2, respectively, as opposed to approximately 1.9 × 10-3 MΩ cm2 and 4.2 × 10-3 MΩ cm2, respectively, after ageing in air. This was attributed to the presence of compressive stresses at the specimen surface after LSP treatment. Stress values were determined from XRD measurements.
Showing items related by title, author, creator and subject.
Influence of the microstructure and laser shock processing (LSP) on the corrosion behaviour of the AA2050-T8 aluminium alloy AMAR, Hassan; KRAWIEC, Halina; JOSSE, Claudie; PEYRE, Patrice; DA SILVA, S. N.; DICK, Luis Federico (Elsevier, 2011)The corrosion behaviour of AA2050-T8 was studied after polishing and after laser shock processing (LSP) treatment using the electrochemical microcell technique and the SVET. After polishing, pitting at constituent particles ...
HFAIEDH, Neila; PEYRE, Patrice; SONG, Hongbin; POPA, Ioana; JI, Vincent; VIGNAL, Vincent (Elsevier, 2015)Laser shock processing is a recently developed surface treatment designed to improve the mechanical properties and fatigue performance of materials, by inducing a deep compressive residual stress field. The purpose of this ...
PEYRE, Patrice; BERTHE, Laurent; VIGNAL, Vincent; POPA, Ioana; BAUDIN, T. (IOP Publishing, 2012)Laser shock processing is now a recognized surface treatment for improving fatigue or corrosion behaviour of metallic materials through the generation of a compressive stress field. In turn, the analysis of shock wave ...
PEYRE, Patrick; BERTHE, Laurent; VIGNAL, Vincent; POPA, Ioana; BAUDIN, Thierry (IOP Publishing, 2012)Laser shock processing (LSP) is now a recognized surface treatment for improving fatigue or corrosion behaviour of metallic materials through the generation of a compressive stress field. In turn, the analysis of shock ...
COTTON, Dominique; JACQUET, Philippe; FAURE, Sébastien; VIGNAL, Vincent (Elsevier, 2017)The carburizing of tantalum samples under different carbon flow rates has highlighted the influence of the carbon flow rate on the structure of tantalum carbides. XRD analyses enabled the identification of surface structures ...