Characterization of CrN/CrAlN/Cr2O3 Multilayers Coatings Synthesized by DC Reactive Magnetron Sputtering
TypeCommunications avec actes
The CrN/CrAlN/Cr2O3 multilayer coatings were deposited by reactive magnetron sputtering DC on 90CrMoV8 stainless steel under various oxygen flow rates. The structure and crystalline phases are characterized by the x-ray diffractometer. Through SEM, a dense and coherent is revealed in CrN/CrAlN/Cr2O3 multilayer coatings. The friction and wear behaviors obtained with the ball-on-disc test show that all multilayer films exhibit a good wear resistance, especially the one with an oxygen flow rate of 10 sccm. Nevertheless, in sea water the film without a top layer of Cr2O3 have the lowest coefficient of friction. This behavior is attributed to the interfacial strengthening and the existence of the upper passivation layer Cr2O3. Adding to that, the film obtained under an oxygen flow rate of 10 sccm show the lowest grain size and the maximum hardness and elastic modulus could Respectively, 45 and 417 GPa.
Files in this item
Showing items related by title, author, creator and subject.
Effect of substrate bias voltage on the microstructure and tribological properties of CrN coatings AOUADI, Khalil; NOUVEAU, Corinne; BESNARD, Aurélien; TLILI, Brahim; CHAFRA, Moez (Lavoisier, 2016)Microstructure, wear and friction coefficient of cr-based magnetron sputtered layers. CrN films were deposited on stainless steel and silicon substrates via magnetron reactive sputtering under a systematic variation of the ...
Influence of Substrate Bias Voltage on Corrosion and Wear Behavior of Physical Vapor Deposition CrN Coatings AOUADI, Khalil; TLILI, Brahim; NOUVEAU, Corinne; BESNARD, Aurélien; CHAFRA, Moez; SOULI, Rania (Springer Verlag - ASM International, 2019)The objective of the present paper is to study the influence of the substrate bias voltage on the microstructure, composition, deposition rate, tribological and corrosion properties of CrN coatings obtained by DC magnetron ...
TLILI, Brahim; NOUVEAU, Corinne; GUILLEMOT, Gildas; BESNARD, Aurélien; BARKAOUI, Abdelwahed (Springer, 2018)The control of residual stresses has been seldom investigated in multilayer coatings dedicated to improvement of wear behavior. Here, we report the preparation and characterization of superposed structures composed of Cr, ...
TLILI, Brahim; NOUVEAU, Corinne; BENLATRECHE, Yacine; MUSTAPHA, Nasri; LAMBERTIN, Michel (2009)In the present investigation, novel Cr/CrN, CrN/CrAlN and Cr/CrN/CrAlN multilayered coatings thin films have been developed by dual RF magnetron sputtering. They consist of superposing Cr, CrN and CrAlN layers of 50–500nm ...
TLILI, Brahim; NASRI, Mustapha; AYARI, F.; NOUVEAU, Corinne (Praise Worthy Prize S.r.l., 2008)Nowadays, most surface treatments are realized through vapor deposition techniques as thin hard coatings to guarantee; high surface hardness, low friction coefficient and improve wear resistance. Several experimental ...