Fatigue Crack Initiation and Propagation
Chapitre d'ouvrage scientifique
Author
DOQUET, VéroniqueHENAFF, Gilbert 
PALIN-LUC, ThierryRISBET, MarionAbstract
The resistance of metal alloys to fatigue can be classified into four major regimes: low-cycle fatigue (or short life), limited resistance (between 10^5 and 10^6 cycles), high-cycle fatigue (between 10^6 and 10^7 cycles) and gigacycle (more than 10^7 cycles). This chapter introduces the basic concepts of cyclic mechanical behavior, crack initiation and propagation in these different regimes.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lecture; ; ; ;FAVIER, Véronique; PALIN-LUC, Thierry; (Elsevier, 2021)
A method coupling experiments and simulations, is developed to characterize the yield stress and strain hardening of several metals loaded at 10⁶ s−ⁱ and < 25 ns, typically involved during Laser Shock Peening. It was applied ...
-
Article dans une revue avec comité de lecture;PALIN-LUC, Thierry; RANC, Nicolas; ; ; ; ; (Elsevier BV, 2025-04)
Ultrasonic fully reversed tension fatigue tests have been performed in the Very High Cycle Fatigue (VHCF) regime (Nr> 1E7 − 1E8 cycles) on Ti-6Al4V specimens containing a controlled internal notch. Two sets of samples have ...
-
Article dans une revue avec comité de lecture;SAINTIER, Nicolas; PALIN-LUC, Thierry; MOREL, Franck (Elsevier, 2011)
Numerical study of high cycle fatigue behaviour of copper polycrystalline aggre- gates. An analysis of high cycle fatigue behaviour is undertaken via the numerical simulation of polycrystalline aggregates. The metallic ...
-
Article dans une revue avec comité de lecturePALIN-LUC, Thierry; ; RANC, Nicolas (Elsevier, 2011)
Plastic dissipation at the crack tip under cyclic loading is responsible for the creation of an heterogeneous temperature field around the crack tip. A thermomechanical model is proposed in this paper for the theoretical ...
-
Communication avec acteAGBESSI, Komlan; SAINTIER, Nicolas; PALIN-LUC, Thierry (2013)
This study provides an analysis of high cycle multiaxial fatigue crack initiation modes based on SEM observations.The statistical study of crack initiation preferential sites shows that grains with multiple slip have a ...