Etude des propriétés microstructurales, mécaniques, thermiques et de la porosité des couches minces de CrAlN déposées par PVD sous différents pourcentages d’aluminium
TypeCommunications avec actes
Several experimental investigations have led to the development of CrAlN (Chrome Aluminum Nitride) hard coatings by varying the aluminum target bias voltage, in preference to the traditional CrN coating. The present work enabled characterisation by physical and mechanical techniques (XRD, AFM, MEB, nano-indentation, Young’s modulus, thermal propriety, Stress, porosity, etc.). Moreover, in order to find improved the adhesion of the different deposition condition of the coatings. The results obtained in this work demonstrate that variation in proportion to aluminum alter the resulting columnar morphology and porosity of the coatings. The thermal properties and the physical property are greatly affected by these morphological alterations. The comparison between the different coating microstructures of CrAlN coatings (columnar and fine-grained) reveals advantages for the fine-grained structure. The results are better wear protection and less profile deviation. Correlation between aluminum proportions in CrAlN coatings and his thermal properties revealed that the conductivity and the diffusivity are influenced primarily by size and shape distribution of the pores and secondarily by decrease of the stitch parameter dimension.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Experimental investigation of the mechanical micro structural and thermal properties of thin CrAIN layers deposited by PVD technique for various aluminum percentages GHRIB, Taher; TLILI, Brahim; NOUVEAU, Corinne; BENLATRECHE, Yacine; LAMBERTIN, Michel; YACOUBI, Noureddine; ENNASRI, M. (Elsevier, 2009)The thin film of chromium nitride and their derivatives obtained by the filing process physical vapor deposition attract more and more attention from industry given their high resistance to wear. This quality of these ...
BRAYEK, A.; TLILI, Brahim; GHRIB, Taher; NOUVEAU, Corinne (EDP Sciences, 2012)In this work we present the technique of magnetron vapor deposition and the effect of several deposition parameters on the structural and morphological properties of prepared thin films. It was noted that the deposition ...
TLILI, Brahim; NOUVEAU, Corinne; WALOCK, Michael J.; NASRI, M.; GHRIB, Taher (Elsevier, 2012)Cr/CrN/CrAlN, CrN/CrAlN and Cr/CrN thin layers were deposited by PVD (Physical Vapor Deposition). The multilayers were obtained from the combined deposition of different layers Cr, CrN and CrAlN thick films on on AISI4140 ...
TLILI, Brahim; NOUVEAU, Corinne; BENLATRECHE, Yacine; MUSTAPHA, Nasri; LAMBERTIN, Michel (2009)In the present investigation, novel Cr/CrN, CrN/CrAlN and Cr/CrN/CrAlN multilayered coatings thin films have been developed by dual RF magnetron sputtering. They consist of superposing Cr, CrN and CrAlN layers of 50–500nm ...
Correlation between thermal properties and aluminum fractions in CrAlN layers deposited by PVD technique TLILI, Brahim; MUSTAPHA, Nasri; NOUVEAU, Corinne; BENLATRECHE, Yacine; GUILLEMOT, Gildas; LAMBERTIN, Michel (Elsevier, 2010)The CrAlN coatings are a good alternative to conventional CrN coatings especially for high temperature oxidation-resistance applications. Different CrAlN coatings were deposited on silicon (100) by PVD (Physical vapor ...