Wear and Corrosion Resistance of CrN-based Coatings Deposited by R.F Magnetron Sputtering
Type
Articles dans des revues avec comité de lectureAbstract
A comparative study was conducted to evaluate the performances against wear and corrosion of CrN, CrMoN, CrZrN, CrVN single layer thin films. The latest are synthesized onto steel substrates (DIN 90CrMoV8), using R.F reactive magnetron co-sputtering. The experimental work was achieved using ball-on-disc configuration in dry conditions against WC balls. The main conclusions are: (i) electrochemical tests in 0.3 wt.% NaCl solution indicated that CrZrN are improved anticorrosion performance when compared to CrN, while CrMoN demonstrated a poor corrosion resistance;(ii) the CrN coating presents the better tribological properties when compared to the ternary nitride coatings.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
BELIARDOUH, Nasser Eddine; BOUZID, Kheireddine; NOUVEAU, Corinne; TLILI, Brahim; WALOCK, Michael J. (Elsevier, 2015)CrN/CrAlN and Cr/CrN/CrAlN multilayers were grown with dual RF magnetron sputtering. The application of these multilayers will be wood machining of green wood. That is why ball-on-disc and electrochemical tests in NaCl ...
-
RAMOUL, Chams Eddine; BELIARDOUH, Nasser Eddine; BAHI, R.; NOUVEAU, Corinne; DJAHOUDI, Abdelghani; WALOCK, Michael J. (Informa UK Limited, 2018)Zirconium nitride (ZrN) thin films were deposited by reactive RF magnetron sputtering on Ti-6Al-4V and Si (100) substrates for potential use in biomedical applications. The tribological behaviour was evaluated against ...
-
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Scientific Bulgarian Communications, 2014)The sliding tribological behaviour of Cr-(WC-Co) coating against wood (beech) as counterpart was investigated using a duplex treatment of low carbon steel(DIN 18CrMo4). The duplex treatment consists of LPC (low pressure ...
-
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; WALOCK, Michael J.; JACQUET, Philippe (elsevier, 2014)The objective of this work is to study the improvement of the tribological properties of low alloy steel using a duplex treatment of lowpressure carburizing and the deposition of a Cr–(WC–Co) coating by dual RF magnetron ...
-
GRAIRIA, Amina; BELIARDOUH, Nasser Eddine; ZAHZOUH, Moussa; NOUVEAU, Corinne; BESNARD, Aurélien (IOP Puiblishing, 2018)WCparticles reinforced Fe-based metal matrix composites were synthesized by powder metallurgy process. The microstructure and composition of the specimens were analyzed and the wear-resistant properties againstWCand alumina ...