Wear and Corrosion Resistance of CrN-based Coatings Deposited by R.F Magnetron Sputtering
TypeArticles dans des revues avec comité de lecture
A comparative study was conducted to evaluate the performances against wear and corrosion of CrN, CrMoN, CrZrN, CrVN single layer thin films. The latest are synthesized onto steel substrates (DIN 90CrMoV8), using R.F reactive magnetron co-sputtering. The experimental work was achieved using ball-on-disc configuration in dry conditions against WC balls. The main conclusions are: (i) electrochemical tests in 0.3 wt.% NaCl solution indicated that CrZrN are improved anticorrosion performance when compared to CrN, while CrMoN demonstrated a poor corrosion resistance;(ii) the CrN coating presents the better tribological properties when compared to the ternary nitride coatings.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Tribological and electrochemical performances of Cr/CrN and Cr/CrN/CrAlN multilayer coatings deposited by RF magnetron sputtering BELIARDOUH, Nasser Eddine; BOUZID, Kheireddine; NOUVEAU, Corinne; TLILI, Brahim; WALOCK, Michael J. (Elsevier, 2015)CrN/CrAlN and Cr/CrN/CrAlN multilayers were grown with dual RF magnetron sputtering. The application of these multilayers will be wood machining of green wood. That is why ball-on-disc and electrochemical tests in NaCl ...
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Scientific Bulgarian Communications, 2014)The sliding tribological behaviour of Cr-(WC-Co) coating against wood (beech) as counterpart was investigated using a duplex treatment of low carbon steel(DIN 18CrMo4). The duplex treatment consists of LPC (low pressure ...
GRAIRIA, Amina; BELIARDOUH, Nasser Eddine; ZAHZOUH, Moussa; NOUVEAU, Corinne; BESNARD, Aurélien (IOP Puiblishing, 2018)WCparticles reinforced Fe-based metal matrix composites were synthesized by powder metallurgy process. The microstructure and composition of the specimens were analyzed and the wear-resistant properties againstWCand alumina ...
A study of the wear performance of duplex treated commercial low-alloy steel against alumina and WC balls BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; WALOCK, Michael J.; JACQUET, Philippe (elsevier, 2014)The objective of this work is to study the improvement of the tribological properties of low alloy steel using a duplex treatment of lowpressure carburizing and the deposition of a Cr–(WC–Co) coating by dual RF magnetron ...
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Emerald Group, 2016)Purpose – The purpose of this technical paper is to investigate the friction and wear behavior of inexpensive and durable cutting tools, developed for wood machining using duplex treatment. Design/methodology/approach – ...