Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime
TypeArticles dans des revues avec comité de lecture
This paper presents an analytical model for assessing the corrosion fatigue crack initiation life on a martensitic stainless steel X12CrNiMoV12-3 in high cycle fatigue regime (between 105 and 107 cycles). Based on in-situ electrochemical measurements during corrosion fatigue tests in NaCl aqueous solution, the corrosion fatigue crack initiation mechanism was identified. Two main stages were investigated: (i) the fracture of the passive film by slip bands and (ii) the free dissolution of the metal developing fatigue crack initiation from a critical corrosion defect. The depassivation stress threshold corresponds to the median fatigue strength at 107 cycles for fatigue corrosion tests. For an applied stress range less than this threshold, the depassivation phenomenon was not observed at 107 cycles and no crack initiation occurred. The proposed model takes into account the depassivation process induced by the slip bands emergence at the specimen surface and the corrosion rate under cyclic loading. The experimental results are compared to the proposed model taking into account mechanical and electrochemical material parameters.
Showing items related by title, author, creator and subject.
EL MAY, Mohamed; SAINTIER, Nicolas; PALIN-LUC, Thierry; DEVOS, Olivier (Wiley, 2015)This paper proposes a volumetric high cycle fatigue (HCF) strength criterion able to quantify the influence of natural corrosion pits on the fatigue limit of a martensitic stainless steel with high mechanical strength. ...
Effect of Corrosion on the High Cycle Fatigue Strength of Martensitic Stainless Steel X12CrNiMoV12-3 EL MAY, Mohamed; PALIN-LUC, Thierry; SAINTIER, Nicolas; DEVOS, Olivier (Elsevier, 2012)This paper addresses the effects of corrosion on the high cycle fatigue (HCF) strength of a high mechanical strength martensitic stainless steel (X12CrNiMoV12-3) that is used in aeronautic applications. HCF tests (between ...
In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth MESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; RANC, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves (2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...
BIDOUARD, Hadrien; PALIN-LUC, Thierry; SAINTIER, Nicolas; DUMAS, Christian; EL DSOKI, Chalid; KAUFMANN, Heinz; SONSINO, Cetin Morris (Carl Hanser Verlag, 2009)Fatigue tests were performed on ferritic bainitic steel notched specimens (Kt = 2.5) under load controlled constant amplitude loading. These tests show that under constant amplitude tension compression loading, periodical ...
Overload effects on a ferritic-baintic steel and a cast aluminium alloy: two very different behaviours SAINTIER, Nicolas; PALIN-LUC, Thierry; EL DSOKI, Chalid; BIDOUARD, Hadrien; KAUFMANN, Heinz; DUMAS, C.; VÖLLMECKE, F.J.; SONSINO, Cetin Morris (Wiley, 2011)Load controlled fatigue tests were performed up to 107 cycles on flat notched specimens (Kt =2.5) under constant amplitude and variable amplitude loadings with and without periodical overloads. Two materials are studied: ...