Effects of LCF Loadings on the HCF Life of Notched Specimens in Ferritic-Bainitic Steel
Article dans une revue avec comité de lecture
Fatigue tests were performed on ferritic bainitic steel notched specimens (Kt = 2.5) under load controlled constant amplitude loading. These tests show that under constant amplitude tension compression loading, periodical overloads application have a detrimental effect on the fatigue crack initiation strength for fully reversed load ratio (R σ = — 1), while they have no influence under pulsating loading (R σ = 0). A finite element analysis shows that in the fully reversed tension (R σ = — 1), the stabilized cyclic behaviour at the notch root is an elastic-plastic shakedown while elastic shakedown is obtained under pulsated regime (R σ = 0), so that we can consider that the local cyclic behaviour has an influence on the overload effect. However, the overload application does not imply a remarkable modification of the stress and strain field under the subsequent constant amplitude loading and can not explain such a fatigue strength decrease in fully reversed tension.
Files in this item
Showing items related by title, author, creator and subject.
Article dans une revue avec comité de lectureBIDOUARD, Hadrien; PALIN-LUC, Thierry; SAINTIER, Nicolas; KAUFMANN, Heinz; DUMAS, Christian; EL DSOKI, Chalid; KAUFMANN, Heinz; SONSINO, Cetin Morris (2009)Fatigue tests were performed on ferritic bainitic steel notched specimens (Kt = 2.5) under load controlled constant amplitude loading. These tests show that under constant amplitude tension compression loading, periodical ...
Overload effects on a ferritic-baintic steel and a cast aluminium alloy: two very different behaviours Article dans une revue avec comité de lectureSAINTIER, Nicolas; PALIN-LUC, Thierry; EL DSOKI, Chalid; BIDOUARD, Hadrien; KAUFMANN, Heinz; DUMAS, C.; VÖLLMECKE, F.J.; SONSINO, Cetin Morris (Wiley-VCH Verlag, 2011)Load controlled fatigue tests were performed up to 107 cycles on flat notched specimens (Kt =2.5) under constant amplitude and variable amplitude loadings with and without periodical overloads. Two materials are studied: ...
In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth Article dans une revue avec comité de lectureMESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; RANC, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves (Wiley-Blackwell, 2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...
Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime Article dans une revue avec comité de lectureEL MAY, Mohamed; SAINTIER, Nicolas; PALIN-LUC, Thierry; DEVOS, Olivier; BRUCELLE, Olivier (Elsevier, 2018)This paper presents an analytical model for assessing the corrosion fatigue crack initiation life on a martensitic stainless steel X12CrNiMoV12-3 in high cycle fatigue regime (between 105 and 107 cycles). Based on in-situ ...
Effect of Corrosion on the High Cycle Fatigue Strength of Martensitic Stainless Steel X12CrNiMoV12-3 Article dans une revue avec comité de lectureEL MAY, Mohamed; PALIN-LUC, Thierry; SAINTIER, Nicolas; DEVOS, Olivier (Elsevier, 2012)This paper addresses the effects of corrosion on the high cycle fatigue (HCF) strength of a high mechanical strength martensitic stainless steel (X12CrNiMoV12-3) that is used in aeronautic applications. HCF tests (between ...