Plasma Nitriding of 90CrMoV8 Tool Steel for the Enhancement of Corrosion Resistance
Type
Articles dans des revues avec comité de lectureAuthor
RAM MOHAN RAO, K.NOUVEAU, CorinneKHANNA, A.S.ANEJA, Karanveer S.TRINADH, KalimiAbstract
In the present studies, efforts were made to improve corrosion resistance of 90CrMoV8 tool steel by following plasma nitriding. Plasma nitriding of this steel at 500 oC for6and 8 h significantly improved the corrosion resistance when compared to the as-received steel. X-ray diffraction reveals γ′ (Fe, Cr)4 N) and ε ((Fe, Cr) 2–3 N) phases formed after nitriding. Potentiodynamic polarization tests in 3.5% NaCl reveal that plasma nitriding significantly improved the corrosion resistance as compared to untreated steel. The improvement in corrosion resistance may be attributed to the N solid solution and the presence of Fe-nitrides formed in the compound layer
Files in this item
Collections
Related items
Showing items related by title, author, creator and subject.
-
(Elsevier BV, 2019)The present concerns surface modification of low alloy CrMoV steel by following the route of plasma nitriding for the improvement of hardness. Plasma nitriding was performed at a low temperature of 450 oC. The maximum ...
-
(IOP Publishing, 2019)This study presents the effect of plasma nitriding on corrosion resistance of low alloy 90CrMoV8 steel. At a selected temperature of 500 °C, nitriding was performed by varying the exposure time. X-ray diffraction of nitrided ...
-
(Springer, 2020)This study presents the plasma nitriding of Cr–Mo–V tool steel to protect it from environmental degradation. The steel samples after metallographic polishing were nitrided in the glow discharge plasma of N2 and H2 gas ...
-
(Elsevier BV, 2019)Surface modification of tool steel had been performed by utilizing plasma nitriding at elevated temperature by varying the exposure time. The nitrided steel had shown significantly enhanced corrosion resistance properties. ...
-
(Elsevier BV, 2021)In this study the effects on resistance to corrosion of a low alloy steel after plasma nitriding has been reported. Nitriding was performed at a low temperature of 450 °C and also at 520 °C for the same duration of 10 h ...