Electrochemical study on the corrosion resistance of surface modified Cr-Mo-V steel by elevated temperature plasma nitriding
Article dans une revue avec comité de lecture
This study presents the effect of plasma nitriding on corrosion resistance of low alloy 90CrMoV8 steel. At a selected temperature of 500 °C, nitriding was performed by varying the exposure time. X-ray diffraction of nitrided steel revealed the presence of Fe, γ′ (Fe, Cr)4Nand ε-(Fe, Cr)2–3N) phases. The cross section of the nitrided steel was analyzed by scanning electron microscope. To understand the effect on corrosion resistance, potentiodynamic polarization along with the electrochemical impedance spectroscopy (EIS) was performed in 3.5% NaCl. The corrosion resistance of the nitrided steel was found to be much higher than the as-received steel. It was also found that the steel nitrided for shorter duration of 6 h has better corrosion resistance than that for 8 h. This enhancement of corrosion resistance may be attributed to the presence of nitrogen in solid solution, γ′-(Fe, Cr)4Nand ε-(Fe, Cr)2–3Nphases.
Showing items related by title, author, creator and subject.
Article dans une revue avec comité de lectureRAM MOHAN RAO, K.; NOUVEAU, Corinne; TRINADH, Kalimi (Elsevier, 2019)The present concerns surface modification of low alloy CrMoV steel by following the route of plasma nitriding for the improvement of hardness. Plasma nitriding was performed at a low temperature of 450 oC. The maximum ...
Article dans une revue avec comité de lectureRAM MOHAN RAO, K.; NOUVEAU, Corinne; KHANNA, A.S.; ANEJA, Karanveer S.; TRINADH, Kalimi (Elsevier, 2020)In the present studies, efforts were made to improve corrosion resistance of 90CrMoV8 tool steel by following plasma nitriding. Plasma nitriding of this steel at 500 oC for6and 8 h significantly improved the corrosion ...
Article dans une revue avec comité de lectureTRINADH, Kalimi; NOUVEAU, Corinne; RAO, K. Ram Mohan (Elsevier, 2021)In this study the effects on resistance to corrosion of a low alloy steel after plasma nitriding has been reported. Nitriding was performed at a low temperature of 450 °C and also at 520 °C for the same duration of 10 h ...
Article dans une revue avec comité de lectureRAO, K. Ram Mohan; NOUVEAU, Corinne; TRINADH, Kalimi (2020)This study presents the plasma nitriding of Cr–Mo–V tool steel to protect it from environmental degradation. The steel samples after metallographic polishing were nitrided in the glow discharge plasma of N2 and H2 gas ...
Article dans une revue avec comité de lectureRAO, K. Ram Mohan; TRINADH, Kalimi; NOUVEAU, Corinne (Elsevier, 2019)Surface modification of tool steel had been performed by utilizing plasma nitriding at elevated temperature by varying the exposure time. The nitrided steel had shown significantly enhanced corrosion resistance properties. ...