Elevated temperature plasma nitriding and effects on electrochemical properties of steel
Type
Articles dans des revues avec comité de lectureAuthor
RAO, K. Ram MohanTRINADH, KalimiNOUVEAU, CorinneAbstract
Surface modification of tool steel had been performed by utilizing plasma nitriding at elevated temperature by varying the exposure time. The nitrided steel had shown significantly enhanced corrosion resistance properties. X-ray diffraction (XRD) had revealed the presence of FexN (x = 2–3, 4) in the surface modified microstructure after nitriding. In an environment of NaCl potentiodynamic polarization and impedance (EIS) tests of steel with and without nitriding had been performed. Both these tests had shown the improved resistance to corrosion of the steel after nitriding.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
(Elsevier BV, 2019)The present concerns surface modification of low alloy CrMoV steel by following the route of plasma nitriding for the improvement of hardness. Plasma nitriding was performed at a low temperature of 450 oC. The maximum ...
-
(Elsevier BV, 2020)In the present studies, efforts were made to improve corrosion resistance of 90CrMoV8 tool steel by following plasma nitriding. Plasma nitriding of this steel at 500 oC for6and 8 h significantly improved the corrosion ...
-
(IOP Publishing, 2019)This study presents the effect of plasma nitriding on corrosion resistance of low alloy 90CrMoV8 steel. At a selected temperature of 500 °C, nitriding was performed by varying the exposure time. X-ray diffraction of nitrided ...
-
(Springer, 2020)This study presents the plasma nitriding of Cr–Mo–V tool steel to protect it from environmental degradation. The steel samples after metallographic polishing were nitrided in the glow discharge plasma of N2 and H2 gas ...
-
(Elsevier BV, 2019)Present study concerns with the effect of plasma nitriding on hardness of low alloy steel. Plasma nitriding had been performed at elevated temperature of 500 C which improved the hardness to 1200 Hv. The case depth was ...