Effects of plasma nitriding on low alloy Cr-Mo-V steel
Article dans une revue avec comité de lecture
In this study the effects on resistance to corrosion of a low alloy steel after plasma nitriding has been reported. Nitriding was performed at a low temperature of 450 °C and also at 520 °C for the same duration of 10 h in the plasma of nitrogen and hydrogen (80:20) gas mixture. Sample holder was biased at -250 V and the working pressure was kept at around 500 Pa. After nitriding the steel samples along with the bare steel were exposed to X-ray diffraction (XRD) to understand the phase formation. For the assessment of corrosion resistance properties potentiodynamic polarization tests of the bare and plasma nitrided steels in 3.5% NaCl electrolyte were performed. Nitriding at 520 °C had shown the best corrosion resistance. However, broad passivation region had been shown after nitriding at 450 °C.
Files in this item
Showing items related by title, author, creator and subject.
Electrochemical study on the corrosion resistance of surface modified Cr-Mo-V steel by elevated temperature plasma nitriding Article dans une revue avec comité de lectureTRINADH, Kalimi; NOUVEAU, Corinne; KHANNA, Anand Sawroop; ANEJA, Karanveer S; RAO, K Ram Mohan (IOP Publishing Ltd, 2019)This study presents the effect of plasma nitriding on corrosion resistance of low alloy 90CrMoV8 steel. At a selected temperature of 500 °C, nitriding was performed by varying the exposure time. X-ray diffraction of nitrided ...
Article dans une revue avec comité de lectureRAM MOHAN RAO, K.; NOUVEAU, Corinne; KHANNA, A.S.; ANEJA, Karanveer S.; TRINADH, Kalimi (Elsevier, 2020)In the present studies, efforts were made to improve corrosion resistance of 90CrMoV8 tool steel by following plasma nitriding. Plasma nitriding of this steel at 500 oC for6and 8 h significantly improved the corrosion ...
Article dans une revue avec comité de lectureRAO, K. Ram Mohan; NOUVEAU, Corinne; TRINADH, Kalimi (2020)This study presents the plasma nitriding of Cr–Mo–V tool steel to protect it from environmental degradation. The steel samples after metallographic polishing were nitrided in the glow discharge plasma of N2 and H2 gas ...
Article dans une revue avec comité de lectureRAO, K. Ram Mohan; TRINADH, Kalimi; NOUVEAU, Corinne (Elsevier, 2019)Surface modification of tool steel had been performed by utilizing plasma nitriding at elevated temperature by varying the exposure time. The nitrided steel had shown significantly enhanced corrosion resistance properties. ...
Article dans une revue avec comité de lectureRAM MOHAN RAO, K.; NOUVEAU, Corinne; TRINADH, Kalimi (Elsevier, 2019)The present concerns surface modification of low alloy CrMoV steel by following the route of plasma nitriding for the improvement of hardness. Plasma nitriding was performed at a low temperature of 450 oC. The maximum ...