In vitro corrosion response of CoCrMo and Ti-6Al-4V orthopedic implants with Zr columnar thin films
Article dans une revue avec comité de lecture
Auteur
Date
2022Journal
Surface and Coatings TechnologyRésumé
This study focuses on the functionalized modification of Ti-6Al-4V and CoCrMo alloys substrates widely used by the biomedical domain as total joint replacements (TJRs) of the hip and knee. To improve the corrosion resistance of these devices, nanostructured columnar zirconium (Zr) thin films were produced by oblique angle deposition (OAD) using DC magnetron sputtering to model the particular design of the joint. The influence of the angular distribution of the incoming particle flux on the resulting film morphology (column tilt angle, porosity) and electrochemical behavior was studied by varying the substrates inclination angle θ from 15 to 90°. The experimental deposition process was reproduced by kinetic Monte Carlo (kMC) models. With the increase of the flux incidence angle α from 0 to 70°, the film thickness and the column tilt angle β vary in agreement with the theoretical models. Additionally, the corrosion behavior of uncoated and Zr-coated alloys (CoCrMo and Ti-6Al-4V) was compared through open circuit potential chronopotentiometry and electrochemical polarization test in NaCl 0.9% solution at 37 °C. It was found that the corrosion protection was successfully improved by the presence of the films. The variation of the corrosion behavior with the flux incidence angle is explained by the changes in the film density.
Fichier(s) constituant cette publication
- Nom:
- LABOMAP_SCT_2022_RAHMOUNI.pdf
- Taille:
- 3.287Mo
- Format:
- Fin d'embargo:
- 2022-09-03
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureWe investigated the effect of film thickness on the structure and properties of VN coatings deposited by magnetron sputtering in an argon and nitrogen atmosphere. The nitrogen percentage was changed between 10 and 20%. ...
-
Article dans une revue avec comité de lectureAISSANI, Linda; ALHUSSEIN, Akram; AYAD, Abdelhak; ZGHEIB, Elia; BELGROUNE, Ahlam; ZAABAT, Mourad; BARILLE, Régis; NOUVEAU, Corinne (Elsevier BV, 2021)Titanium nitride films were deposited by reactive magnetron sputtering on Si (100) wafers, glass and Ti6Al4V substrates. The film deposition was carried out in a gas mixture of Ar and N2. The nitrogen content was varied ...
-
Article dans une revue avec comité de lectureAISSANI, Linda; ALHUSSEIN, Akram; RADJEHI, Lamia; LAKDHAR, Issam; ZGHEIB, Elia; NOUVEAU, Corinne (Elsevier, 2019)Vanadium carbide coatings were deposited by R.F. reactive magnetron sputtering at different nitrogen partial pressures. The structures and the mechanical and tribological behaviour of these coatings were studied. By using ...
-
Effect of carbon content on structural, mechanical and tribological properties of Cr-V-C-N coatings Article dans une revue avec comité de lectureAISSANI, Linda; ALHUSSEIN, Akram; BELGROUNE, Ahlam; ZGHEIB, Elia; BARILLE, Regis; NOUVEAU, Corinne; MONTAGNE, Alex (Elsevier BV, 2021)Cr-V-C-N thin films were deposited on XC100 steel and Si(100) wafers by a radio frequency magnetron sputtering technique using chromium and vanadium targets in an Ar/N2/CH4 mixture atmosphere. The microstructure, mechanical ...
-
Communication sans acteFELLAH, Mamoun; AISSANI, Linda; LABAIZ, Mohamed; IOST, Alain; LAKMINE, F.; ABDUL SAMAD, Mohammed; NOUVEAU, Corinne; MONTAGNE, Alex (2016)The current research was undertaken to study the improvement of the tribological behavior of nanocrystalline bioceramic, α-alumina sample, produced by the calculations of gibbsite at different temperatures (300 to 1200°C), ...