Effect of Corrosion on the High Cycle Fatigue Strength of Martensitic Stainless Steel X12CrNiMoV12-3
Article dans une revue avec comité de lecture
This paper addresses the effects of corrosion on the high cycle fatigue (HCF) strength of a high mechanical strength martensitic stainless steel (X12CrNiMoV12-3) that is used in aeronautic applications. HCF tests (between 105 and 107 cycles) were carried out in two environments: (i) in air and (ii) in an aqueous solution (pH = 6) of 0.1 M NaCl + 0.044 M Na2SO4 at a loading frequency of 120 Hz. Surface crack initiation is observed in air, whereas in solution, the crack initiated at corrosion defects. The decrease observed in the corrosion fatigue strength of specimens at 107 cycles was 33% of that of similar specimens tested in air. The electrochemical behaviour of the passive film was investigated during fatigue testing in a NaCl aqueous solution by monitoring the free potential and through electrochemical impedance spectroscopy (EIS). Based on fractography analysis and the EIS tests results, fatigue crack initiation mechanisms in air and in the NaCl aqueous solution were identified. A scenario for fatigue crack initiation is proposed based on the physical evidence. Local passive film ruptures are the cause of the corrosion fatigue crack initiation. The film is broken by material strain from the applied cyclic stress during fatigue testing, causing increased local corrosive attack. This effect has been shown at 10 Hz and 120 Hz because the characteristic time for repassivation for the steel is very low compared to the period of the cyclic loading.
Showing items related by title, author, creator and subject.
Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime Article dans une revue avec comité de lectureEL MAY, Mohamed; SAINTIER, Nicolas; PALIN-LUC, Thierry; DEVOS, Olivier; BRUCELLE, Olivier (Elsevier, 2018)This paper presents an analytical model for assessing the corrosion fatigue crack initiation life on a martensitic stainless steel X12CrNiMoV12-3 in high cycle fatigue regime (between 105 and 107 cycles). Based on in-situ ...
Article dans une revue avec comité de lectureEL MAY, Mohamed; SAINTIER, Nicolas; PALIN-LUC, Thierry; DEVOS, Olivier (Wiley-Blackwell, 2015)This paper proposes a volumetric high cycle fatigue (HCF) strength criterion able to quantify the influence of natural corrosion pits on the fatigue limit of a martensitic stainless steel with high mechanical strength. ...
In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth Article dans une revue avec comité de lectureMESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; RANC, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves (Wiley-Blackwell, 2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...
Overload effects on a ferritic-baintic steel and a cast aluminium alloy: two very different behaviours Article dans une revue avec comité de lectureSAINTIER, Nicolas; PALIN-LUC, Thierry; EL DSOKI, Chalid; BIDOUARD, Hadrien; KAUFMANN, Heinz; DUMAS, C.; VÖLLMECKE, F.J.; SONSINO, Cetin Morris (Wiley-VCH Verlag, 2011)Load controlled fatigue tests were performed up to 107 cycles on flat notched specimens (Kt =2.5) under constant amplitude and variable amplitude loadings with and without periodical overloads. Two materials are studied: ...
Article dans une revue avec comité de lectureBIDOUARD, Hadrien; PALIN-LUC, Thierry; SAINTIER, Nicolas; DUMAS, Christian; EL DSOKI, Chalid; KAUFMANN, Heinz; SONSINO, Cetin Morris (2009)Fatigue tests were performed on ferritic bainitic steel notched specimens (Kt = 2.5) under load controlled constant amplitude loading. These tests show that under constant amplitude tension compression loading, periodical ...