Evolution of microstructure and residual stress during annealing of austenitic and ferritic steels
Article dans une revue avec comité de lecture
Auteur
BACZMANSKI, AndrzejMARCISZKO, MariannaWRÓBEL, Mirosław X.SZTWIERTNIA, KrzysztofBERENT, Katarzyna 
BRAHAM, ChedlyRésumé
In this work the recovery and recrystallization processes occurring in ferritic and austenitic steels were studied. To determine the evolution of residual stresses during material annealing the nonlinear sin 2 ψ diffraction method was used and an important relaxation of the macrostresses as well as the microstresses was found in the cold rolled samples subjected to heat treatment. Such relaxation occurs at the beginning of recovery, when any changes of microstructure cannot be detected using other experimental techniques. Stress evolution in the annealed steel samples was correlated with the progress of recovery process, which significantly depends on the value of stacking fault energy.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lecture; ; ; ; ; ; ; ; ;BRAHAM, Chedly (Elsevier, 2012)
Multi-reflection grazing incidence geometry, referred to as MGIXD, characterized by a small and constant incidence angle, was applied to measure low surface stresses in very thin layers of Al–Mg alloy and CrN coating. These ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ;BRAHAM, Chedly (International Union of Crystallography, 2015)
Multireflection grazing-incidence X-ray diffraction (MGIXD) was used to determine the stress- and strain-free lattice parameter in the surface layer of mechanically treated (polished and ground) tungsten and austenitic ...
-
Article dans une revue avec comité de lecture; ; ; ; ;BRAHAM, Chedly (Elsevier, 2017)
The presented study introduces the development of the multi-reflection grazing-incidence X-ray diffraction method (MGIXD) for residual stress determination. The proposed new methodology is aimed at obtaining more reliable ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ; ; ; ;BRAHAM, Chedly (International Union of Crystallography, 2018)
The main focus of the presented work was the investigation of structure and residual stress gradients in the near-surface region of materials studied by X-ray diffraction. The multireflection method was used to measure ...
-
Article dans une revue avec comité de lecture; ; ; ; ;BRAHAM, Chedly (International Union of Crystallography, 2019)
The multireflection grazing-incidence X-ray diffraction method is used to test surface stresses at depths of several micrometres in the case of metal samples. This work presents new ways of analysing experimental data ...