Topography and wettability characterization of surfaces manufactured by SLM and treated by chemical etching
TypeArticles dans des revues avec comité de lecture
Selective Laser Melting process represents an interesting opportunity in the biomedical field to fabricate customized implants. However, the surface roughness of components obtained through additive manufacturing is a major limitation and affects the surface wettability. In the present work, chemical etching is adopted to deal with such an issue. To do so, the effects of chemical etching parameters (such as immersion time and composition of the solution) on the surface roughness, weight loss and wettability is analyzed. Different samples (obtained through different printing orientations) are considered. The tests show that the roughness and the wetting of the surfaces are improved thanks to chemical etching. As a major result, the most influencing parameters on surface wetting are two: the roughness and the material properties (which vary with samples depth).
Files in this item
Showing items related by title, author, creator and subject.
A Cellular Potts energy-based approach to analyse the influence of the surface topography on single cell motility THENARD, Thomas; CATAPANO, Anita; MESNARD, Michel; ALLENA, Rachele (Elsevier, 2021)cellular scale level, the cell behaviour, especially its migration, is affected by the specificities of the surface of the substrate, such as the stiffness of the surface and its roughness topography. The latter has been ...
In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth MESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; RANC, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves (2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...
Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime EL MAY, Mohamed; SAINTIER, Nicolas; PALIN-LUC, Thierry; DEVOS, Olivier; BRUCELLE, Olivier (Elsevier, 2018)This paper presents an analytical model for assessing the corrosion fatigue crack initiation life on a martensitic stainless steel X12CrNiMoV12-3 in high cycle fatigue regime (between 105 and 107 cycles). Based on in-situ ...
EL MAY, Mohamed; SAINTIER, Nicolas; PALIN-LUC, Thierry; DEVOS, Olivier (Wiley, 2015)This paper proposes a volumetric high cycle fatigue (HCF) strength criterion able to quantify the influence of natural corrosion pits on the fatigue limit of a martensitic stainless steel with high mechanical strength. ...
Effect of Corrosion on the High Cycle Fatigue Strength of Martensitic Stainless Steel X12CrNiMoV12-3 EL MAY, Mohamed; PALIN-LUC, Thierry; SAINTIER, Nicolas; DEVOS, Olivier (Elsevier, 2012)This paper addresses the effects of corrosion on the high cycle fatigue (HCF) strength of a high mechanical strength martensitic stainless steel (X12CrNiMoV12-3) that is used in aeronautic applications. HCF tests (between ...