Effect of interlamellar spacing on the elastoplastic behavior of C70 pearlitic steel: Experimental results and self-consistent modeling
TypeArticles dans des revues avec comité de lecture
The effect of pearlite microstructure characteristics on strength and deformation of C70 pearlitic steel was investigated. Tensile tests under X-ray diffraction coupled with self-consistent model have been used to identify the role of interlamellar spacing on the ferrite plasticity parameters and residual stress induced by plasticity. Tests have been carried out on two pearlitic microstructures with interlamellar spacing Sp = 170 and 230 nm respectively. Ferrite critical shear stresses ðs0c ðaÞÞ are equal to 75–86 MPa for interlamellar spacing Sp = 230 nm and 105–120 MPa for interlamellar spacing Sp = 170 nm. Moreover, the compressive residual stress measured in ferrite phase is higher in elasto-plastically deformed sample (total strain of E11 = 1.2%) having larger interlamellar spacing (rR Fea ¼ 161 MPa for Sp = 230 nm and rR Fea ¼ 77 MPa for Sp = 170 nm).
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
A multireflection and multiwavelength residual stress determination method using energy dispersive diffraction MARCISZKO, Marianna; WAWSZCZAK, Roman; SIDHOM, Habib; BRAHAM, Chedly; WROBEL, Mirosław; WRONSKI, Sebastian; OPONOWICZ, Adrian; GENZEL, Christoph; KLAUS, Manuela; BACZMANSKI, Andrzej (Wiley-Blackwell, 2018)The main focus of the presented work was the investigation of structure and residual stress gradients in the near-surface region of materials studied by X-ray diffraction. The multireflection method was used to measure ...
Application of multireﬂection grazing incidence method for stress measurements in polished Al–Mg alloy and CrN coating MARCISZKO, Marianna; BACZMANSKI, Andrzej; WIERZBANOWSKI, K; WROBEL, Mirosław; BRAHAM, Chedly; CHOPART, J.-P.; LODINI, A; BONARSKI, J; TARKOWSKI, L.; ZAZI, N (Elsevier, 2012)Multi-reﬂection grazing incidence geometry, referred to as MGIXD, characterized by a small and constant incidence angle, was applied to measure low surface stresses in very thin layers of Al–Mg alloy and CrN coating. These ...
Stress distribution correlated with damage in duplex stainless steel studied by synchrotron diffraction during plastic necking ZHAO, Yuchen; LE JONCOUR, L; BACZMANSKI, Andrzej; GADALIŃSKA, E; WRONSKI, Sebastian; PANICAUD, B; FRANÇOIS, M; BRAHAM, Chedly; BUSLAPS, T (Elsevier, 2017)The goal of this work was the determination of lattice strains distribution in two phases of duplex steel during plastic necking. Subsequently, the stress heterogeneity in the neck was studied in order to determine the ...
Stress measurements by multi-reflection grazing-incidence X-ray diffraction method (MGIXD) using different radiation wavelengths and different incident angles MARCISZKO, Marianna; BACZMANSKI, Andrzej; BRAHAM, Chedly; WROBEL, Mirosław; WRONSKI, Sebastian; CIOS, Grzegorz (Elsevier, 2017)The presented study introduces the development of the multi-reflection grazing-incidence X-ray diffraction method (MGIXD) for residual stress determination. The proposed new methodology is aimed at obtaining more reliable ...
Problem of elastic anisotropy and stacking faults in stress analysis using multireflection grazing-incidence X-ray diffraction MARCISZKO, Marianna; BACZMANSKI, Andrzej; MIROSŁAW, Wrobel; SEILER, Wilfrid; BRAHAM, Chedly; WRONSKI, Sebastian; WAWSZCZAK, Roman (International Union of Crystallography, 2015)Multireflection grazing-incidence X-ray diffraction (MGIXD) was used to determine the stress- and strain-free lattice parameter in the surface layer of mechanically treated (polished and ground) tungsten and austenitic ...